PC 02 W2 1180

Smoothed white ceramic mass (clay). It melts well even at temperatures of 1040 ° C. Very plastic suitable for small and large items.

Suitable for making, building, working on boards, hand molding in gypsum molding (molding), forming of presses, sculptural modeling, extrusion, etc. Preferred clay for work with children.

  • Biscuit temperature 980-1040 ° C.
  • Temperature of glaze firing from 1040 to 1180 ° C.
  • Chamotte content more than 10% 0-0.4mm.
  • Packaging - 10 kg in PE envelopes

Recommended glazes: GTR 01, GO 01, GTR 07 (over 1100 ° C), GO 05 (over 1100 ° C), GTR 10, GO 10.

PC 02 W2 1180 S 0-2

Smoothed white ceramic mass (clay).It melts well even at temperatures of 1040 ° C.Very plastic suitable for small and large items.

Suitable for making, building, working on boards, hand molding in gypsum molding (molding), forming of presses, sculptural modeling, extrusion, etc.

  • Biscuit temperature 980-1040 ° C.
  • Temperature of glaze firing from 1040 to 1180 ° C.
  • Chamotte fractions content 0-2mm - above 30%.
  • Packaging - 10 kg in PE envelopes
  • Recommended glazes: GTR 01, GO 01, GTR 07 (over 1100 ° C), GO 05 (over 1100 ° C), GTR 10, GO 10.

    PC 03 W2 1200

    Fine snow white ceramic table. Suitable for small and large items.

    Recommended for gardening, work on boards, sculpture modeling, molding in molding, extruding, etc.

  • Biscuit temperature 980-1100 ° C.
  • Temperature of glaze firing from 1070 to 1230 ° C.
  • Packaging - 10 kg in PE envelopes.
  • Recommended glazes: GTR 01, GO 01, GTR 07 (over 1100 ° C), GO 05 (over 1100 ° C), GTR 10, GO 10.

    PC 03 W2 1200 S 0-2

    Simulated snow white ceramic table. Suitable for small and large items.

    Recommended for gardening, work on boards, sculpture modeling, molding in molding, extruding, etc.

    • Biscuit temperature 980-1100 ° C.
    • Temperature of glaze firing from 1070 to 1230 ° C.
    • Contains a sham fraction of 0 to 2mm over 30%.
    • Packaging - 10 kg in PE envelopes.
    • Produced on request!

    Recommended glazes: GTR 01, GO 01, GTR 07 (over 1100 ° C), GO 05 (over 1100 ° C), GTR 10, GO 10.

    PC 04 W8 1150

    Fine-tempered red-burning ceramic table (toaster clay). Very plastic, suitable for small and medium-sized items (up to 60 cm).Extremely suitable for cutting.

    The red plastic table is designed for cutting, building, plate work, gypsum molding (molding), sculptural modeling extrusion, RAM pressing and rotary presses.

  • Biscuit temperature 800-980 ° C.
  • Temperature of glaze firing - 980-1150 ° C.
  • Chamot content more than 10% 0-0.4mm.
  • Packaging - 10 kg in PE envelopes.
  • Recommended glazes: GTR 07, GO 05

    PC 04 W8 1150 S 0-2

    Simulated red-burning plastic ceramic table.

    Suitable for small and large items up to 1.5m. Suitable for gardening, work on boards, hand molding in gypsum molding (molding), forming of presses, sculptural modeling, extrusion, etc.

  • Biscuit temperature 800-980 ° C.
  • Temperature of glaze firing - 980-1150 ° C.
  • Content of white sham fraction 0-2mm - over 30%.
  • Packaging - 10 kg in PE envelopes.
  • Produced on request!
  • Recommended glazes: GTR 07, GO 05.

    PC 05 W0 1100

    Snow-white, white, fainter table with a high degree of whiteness. Suitable for small and medium-sized products (up to 60 cm). Minimal deformations and shrinkage in a large temperature range.

    Recommended techniques are extrusion, compression of RAM presses and rotary presses, plate work, molding in gypsum molds.

    • Biscuit temperature 1000-1100 ° C.
    • Temperature of glaze firing - 980-1100 ° C.
    • Packaging - 10 kg in PE envelopes.

    Recommended glazes: GTR 07, GO 05.

    PC 08 W1 1220

    Porcelain plastic table, meeting all the toughest requirements for whiteness and visibility. The material has optimal plasticity. Contains special additives that reduce friction in molding and increase the strength and plasticity of the raw.

    It is suitable for molding machine and presses for making of food service, frost-resistant tiles etc.

    • Moisture - 19-21%.
    • Biscuit temperature 980-1100 °C.
    • Temperature of glaze firing 1180-1220 °C.
    • Chamot content more than 10% 0-0.4mm.
    • Packaging - 10 kg in PE envelopes.

    Recommended glazes: GTR 01, GO 01, GTR 07, GO 05.

    PLASTIC CERAMIC BODIES

    Certificates

    All products are accompanied by the necessary documentation certifying their quality, characteristics and purpose.

    Control

    Continuous quality control and chemical analysis from raw material to final product.

    Eco
    The raw materials and additives used in the production are entirely natural products.